東莞市奧亞塑膠原料有限公司

Processing Texts

Injection molding

PREPROCESSING

Drying recommended = Yes, if moisture content of resin exceeds recommended level
Drying temperature = 80°C
Drying time, dehumidified dryer = 2-4 h
Processing moisture content = <0.2 %

PROCESSING

Melt temperature optimum = 290°C
Melt temperature range = 280-300°C
Mould temperature optimum = 100°C
Mould temperature range = 70-120°C

Rheological properties	dry / cond	Unit	Test Standard
Viscosity number	130 / *	cm³/g	ISO 307, 1157, 1628
Moulding shrinkage, parallel	0.3 / *	%	ISO 294-4, 2577
Moulding shrinkage, normal	0.7 / *	%	ISO 294-4, 2577

Mechanical properties	dry / cond	Unit	Test Standard
Tensile Modulus	8800 / 7800	MPa	ISO 527-1/-2
Stress at break	145 / 110	MPa	ISO 527-1/-2
Strain at break	2.5 / 2.6	%	ISO 527-1/-2
Tensile creep modulus			ISO 899-1
1h	* / 7000	MPa
1000h	* / 6000	MPa
Charpy impact strength			ISO 179/1eU
23°C	41 / 41	kJ/m²
-30°C	40 / 40	kJ/m²
Charpy notched impact strength			ISO 179/1eA
23°C	4 / 4	kJ/m²
-30°C	4 / 3	kJ/m²

Thermal properties	dry / cond	Unit	Test Standard
Melting temperature, 10°C/min	245 / *	°C	ISO 11357-1/-3
Glass transition temperature, 10°C/min	90 / -	°C	ISO 11357-1/-2
Temp. of deflection under load, 1.8 MPa	230 / *	°C	ISO 75-1/-2
Coeff. of linear therm. expansion, parallel	23 / *	E-6/K	ISO 11359-1/-2
Coeff. of linear therm. expansion, normal	60 / *	E-6/K	ISO 11359-1/-2
Thermal conductivity of melt	0.26	W/(m K)	-
Spec. heat capacity of melt	2280	J/(kg K)	-

Flammability	dry / cond	Unit	Test Standard
Burning Behav. at 1.5mm nom. thickn.	HB / *	class	IEC 60695-11-10
Thickness tested	1.5 / *	mm	IEC 60695-11-10

Electrical properties	dry / cond	Unit	Test Standard
Volume resistivity	8E12 / 2E10	Ohm*m	IEC 60093
Surface resistivity	* / 3E14	Ohm	IEC 60093
Electric strength	41 / 41	kV/mm	IEC 60243-1

Other properties	dry / cond	Unit	Test Standard
Humidity absorption, 2mm	1.5 / *	%	Sim. to ISO 62
Water absorption, 2mm	5 / *	%	Sim. to ISO 62
Density	1460 / -	kg/m³	ISO 1183
Density of melt	1300	kg/m³	-